Influence of the Co Thickness Layers on the Magnetic and Structural
Properties of Nanocrystalline [Nd-Fe-B-Nb-Cu/Co]×n Films
H. CHIRIAC, M. GRIGORAŞ, M. URSE
Abstract. Some results concerning the influence of the thickness of Co
layers on the structural and magnetic properties of [NdFeBNbCu/Co]×n nanocrystalline films, when the total thickness of NdFeBNbCu layers was of
540 nm and the thickness of Co spacer layers was varied from 2 to 6 nm,
are presented. As compared to the Ta/NdFeBNbCu/Ta films, the multilayer
Ta/[NdFeBNbCu(180 nm)/Co(2 nm)]×3/Ta films annealed at 650°C for 20
minutes exhibit very good hard magnetic properties such as, the coercivity
Hc of about 2.28 T, remanence Mr of about 0.94 T, energy product of 347
kJ/m3 and an increase in the Curie temperature of about 68°C. |